DLP Materials

ROBUST MATERIALS & STRONG, END-USE PARTS

Leveraging the wide array of DLP materials, our team at Bay Area 3D Printing can create durable and intricate end-use parts for any industry.

Smarter Production

Create high strength, flexible, and heat resistant parts for low-volume production.

Heat Resistant

LOCTITE 3D IND403

High modulus tough resin for high temperature resistance.

Colors: Black
Ultimate Tensile Strength: 72 MPa
Elongation at Break: 10%
Tensile Modulus: 2572 MPa
HDT: 80°C

Ultracur3D RG 3280

Ceramic-filled resin with exceptionally high stiffness and temperature resistance.

Colors: White
Ultimate Tensile Strength: 87 MPa
Elongation at Break: 1.3%
Tensile Modulus: 10600 MPa
HDT: 284°C

Tough

LOCTITE 3D 3172

Tough and high impact, for fixtures and tooling.

Colors: Grey
Ultimate Tensile Strength: 39 MPa
Elongation at Break: 105%
Tensile Modulus: 1494 MPa
HDT: 51°C

LOCTITE 3D 3843

High-impact, semi-flexible resin suitable for a broad range of applications.

Colors: Black, Matte Black, Clear
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 43%
Tensile Modulus: 1806 MPa
HDT: 60°C

Stratasys Dura56

Impact resistant and durable photopolymer for functional applications where aesthetics and strength are critical.

Colors: Black
Ultimate Tensile Strength: 44 MPa
Elongation at Break: 78%
Tensile Modulus: 1595 MPa
HDT: 52°C

General Purpose

Somos QuickGen500

Fast-printing, flexible resin for general and functional prototypes.

Colors: Clear
Ultimate Tensile Strength: 20 MPa
Elongation at Break: 42%
Tensile Modulus: 465 MPa
HDT: 62° C

Ultracur3D ST45

Reactive urethane polymer for high-performance functional parts.

Colors: Black
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 21%
Tensile Modulus: 2000 MPa
HDT: 63°C

Somos WeatherX 100

Environmentally durable material designed for end-use parts.

Colors: Black
Ultimate Tensile Strength: 60 ± 0.3 MPa
Elongation at Break: 26% ± 6.0
Tensile Modulus: 2128 ± 154 MPa
HDT: 67° C

Elastomers

LOCTITE 3D IND402

High rebound elastomer with high resilience, ideal for lattice structures.

Colors: Black
Ultimate Tensile Strength: 5.5 MPa
Elongation at Break: 230%
Tensile Modulus: 42 MPa

Medical

LOCTITE 3D MED413

Biocompatible material designed for general medical purposes.

Colors: White
Ultimate Tensile Strength: 46 MPa
Elongation at Break: 51%
Tensile Modulus: 1673 MPa
HDT: 68°C